VASILE GEORGESCU, GABRIEL VASILIEVICI, MIHAELA BOMBOS, CASEN PANAITESCU STUDY OF CO-CR MIXED OXIDES FOR DIFFERENT APPLICATIONS Mixture metal oxide system Co-Cr were prepared by decomposition of the precursor complexes obtained from a mixture Co-Cr nitrates with tartaric acid. The samples were subsequently submitted to chemical analysis, magnetic measurements, IR spectrometry, UV-Vis, thermal analysis, XRD, EXAFS and TPR. At 600oC was identificated a solid solution of CoCr2O4 with Co3O4. With Cu-CrK-edge EXAFS the local structure of samples calcinated of 420oC and 600oC was obtained. By theirs analysis was calculated: the lengths of M-O bounds, number of coordination (N), Debye-Waller factor (A1) and x metallic cations fraction in tetrahedral structures (spinelic centers). The TPR measurements were emphasized the existence of two reduction cycles.